Santoso, Eko Budi (2021) PENGARUH PERBANDINGAN NACL DAN COPPER SULPHATE TERHADAP MATERIAL HILANG PADA PERENDAMAN LOGAM ST41. PENGARUH PERBANDINGAN NACL DAN COPPER SULPHATE TERHADAP MATERIAL HILANG PADA PERENDAMAN LOGAM ST41, 6 (1). pp. 1-6. ISSN 2615-0867

	Text 5012-12123-1-SM.pdf Available under License Creative Commons Attribution Non-commercial Share Alike. Download (268kB)
	Text PENGARUH PERBANDINGAN NACL DAN COPPER SULPHATE TERHADAP MATERIAL HILANG PADA PERENDAMAN LOGAM ST41.pdf Available under License Creative Commons Attribution Non-commercial Share Alike. Download (1MB)

Abstract

Abstrak Dalam menghadapi kemajuan pada era industrialisasi maka ilmu pengetahuan dan teknologi yang berhubungan dengan proses perlindungan dari pengikisian logam oleh material lain atau yang dikenal dengan korosi juga mengalami perkembangan yang pesat. Banyak cara yang dilakukan antara lain dengan pelumasan dan pelapisan, dimana tujuannya adalah mencegah lajunya korosi atau pengikisan yang akan menurunkan sifat terbaik material. Korosi dianggap sebagai suatu kerugian dalam mempertahankan mechanical properties dari suatu material, tetapi masih ada peluang yang bisa dilakukan dengan memanfaatkan korosi. Dalam penelitian ini bertujuan untuk mengetahui pengaruh perbandingan massa antara larutan NaCl dan Cooper Sulphate terhadap material yang hilang pada logam ST 41. Spesimen direndam dengan variasi perbandingan massa antara larutan NaCl dengan Copper Sulphate dengan menggunakan variasi perbandingan antara NaCl dan Copper Sulphate, dengan waktu perendaman adalah 6 jam, 12 jam dan 18 jam. Untuk mengetahui material hilang dilakukan dengan melakukan penimbangan, pengukuran pH dan pengamatan visual hasil perendaman. Dari Penelitian ini didapatkan hasil material hilang paling kecil di dapatkan pada hasil perendaman dengan perbandingan 1:1 dengan material hilang rata rata 0,0025 gr, sedang material hilang terbesar di dapat pada perbandingan 1:3 yaitu sebesar rata rata 0,0235 gram. Secara Visual kekasaran permukaan material yang dikenai perlakuan dimana perbandingan Cooper Sulphate lebih besar, terlihat lebih kasar di banding dengan yang lainnya Kata kunci: Korosi, Baja ST 41, NaCl, Copper Sulphate Abstract In facing the advancement of the industrialization era, science and technology related to the protection process from metal erosion by other materials or known as corrosion, also experienced rapid development. Many ways are done, among others, by lubrication and coating, which aims to prevent the corrosion rate which will reduce the best properties of the material. Corrosion is considered as a loss in maintaining the mechanical properties of a material, but there is still a possibility that it can be done by utilizing corrosion. This study aims to determine the effect of the mass ratio between the NaCl and Cooper Sulfate solutions on the lost material in ST 41 metal. The specimens were immersed with various mass ratios between NaCl and Copper Sulfate solutions using variations in the ratio between NaCl and Copper Sulfate, with immersion times of 6 hours, 12 hours and 18 hours. To find out the missing material, it is done by weighing, measuring the pH and visual observation of the immersion results. From this research, it was found that the smallest loss of material was obtained in the immersion results with a ratio of 1:1 with an average loss of material of Jurnal Teknik Mesin UNISKA Vol. 6 No. 1 Mei 2021 p-ISSN 2502-4922,e-ISSN 2615-0867 15 | 0.0025 grams , while the largest loss of material was obtained at a ratio of 1:3. namely 0.0235 grams Visually the surface roughness Materials that are subjected to treatment in which the Cooper Sulfate ratio is greater, look rougher than others. Keywords : corrosion, Steel ST41, NaCl, Copper Sulphate

Item Type:	Article
Uncontrolled Keywords:	Korosi, Baja ST 41, NaCl, Copper Sulphate
Subjects:	Engineering > Mechanical Engineering
Divisions:	Fakultas Teknologi Industri > Teknik Mesin DIII
Depositing User:	Ms Nunuk Yuli
Date Deposited:	06 Jul 2023 02:55
Last Modified:	06 Jul 2023 02:55
URI:	http://eprints.itn.ac.id/id/eprint/12231

Actions (login required)

View Item