ANALISA PENGARUH KECEPATAN PUTARAN SPINDEL PADA PROSES PEMBUBUTAN RADIUS MENGGUNAKAN RADIUS TOOL POST TERHADAP KEKASARAN PERMUKAAN BAJA S45C

AKHMAD, FAHROBI (2019) ANALISA PENGARUH KECEPATAN PUTARAN SPINDEL PADA PROSES PEMBUBUTAN RADIUS MENGGUNAKAN RADIUS TOOL POST TERHADAP KEKASARAN PERMUKAAN BAJA S45C. Skripsi thesis, Institut Teknologi Nasional Malang.

Text SKRIPSI FAHROBI AKHMAD 15.11.078-dikonversi.pdf Restricted to Registered users only Available under License Creative Commons Attribution Non-commercial Share Alike. Download (4MB) | Request a copy

Abstract

ANALISA PENGARUH KECEPATAN PUTARAN SPINDEL PADA PROSES PEMBUBUTAN RADIUS MENGGUNAKAN RADIUS TOOL POST TERHADAP KEKASARAN PERMUKAAN BAJA S45C Fahrobi Akhmad (15.11.078) Jurusan Teknik Mesin S-1, FTI – Institut Teknologi Nasional Malang Jl. Raya Karanglo KM. 2, Tasikmadu, Kec. Lowokwaru, Kota Malang, Jawa Timur 65153 Email : Fahrobi.26@gmail.com ABSTRAK Mesin Bubut merupakan suatu jenis mesin perkakas yang dalam proses kerjanya menggerakkan benda kerja dan menggunakan mata pahat potong sebagai alat untuk menyayat benda kerja tersebut dimana akan menghasilkan benda kerja berbentuk silindris. Penjepit Pahat merupakan suatu komponen dari mesin bubut yang memiliki fungsi untuk memegang alat potong yang dipergunakan dalam proses pembubutan. Dimana penjepit pahat standar pada mesin bubut pada umumnya memiliki gerakan melintang, membujur, ataupun tirus. Sedangkan dalam pembubutan radius pada mesin bubut terdapat banyak kendala pada prosesnya. Untuk itu diperlukan rancangan Radius Tool Post, yaitu penjepit pahat yang digunakan dalam proses pembubutan radius pada mesin bubut. Dimana dalam penelitian ini yaitu menganalisa rancangan radius tool post terhadap kekasaran permukaan baja S45C dengan variasi bentuk ukuran benda kerja 20 mm, 50 mm, 80 mm dan juga kecepatan putaran spindel 210 rpm, 380 rpm, dan 460 rpm untuk masing-masing spesimen. Hasil dari peneltian menunjukkan pada diameter 20 mm nilai optimal didapatkan pada kecepatan putaran spindel 460 rpm dengan rata-rata nilai kekasaran permukaan yang dihasilkan sebesar 0,80 μm. Pada diameter 50 mm nilai optimal didapatkan pada kecepatan putaran spindel 460 rpm dengan rata-rata nilai kekasaran permukaan yang dihasilkan sebesar 1,34 μm. Dan pada diameter 80 mm nilai optimal didapatkan pada kecepatan putaran spindel 460 rpm dengan rata-rata nilai kekasaran permukaan yang dihasilkan sebesar 1,6 μm. Dapat dilihat dari hasil penelitian bahwa semakin besar diameter benda kerja semakin besar pula kekasaran permukaan, semakin besar kecepatan putaran spindel maka nilai kekasaran permukaan semakin menurun. Dengan demikian dari penelitian yang dilakukan, variasi ukuran diameter dan kecepatan putaran spindel pada pembubutan radius menggunakan radius tool post berpengaruh terhadap nilai kekasaran permukaan yang dihasilkan. Dan juga kekasaran benda hasil proses bubut radius menggunakan radius tool post memenuhi standar nilai kekasaran yang diijinkan yaitu 0,4 – 5.0 μm. Kata kunci : Mesin Bubut, Radius Tool Post, Kekasaran Permukaan ABSTRACT Lathe is a type of machine tool which in the process of working moves a workpiece and used a cutting tool as a tool to cut the workpiece which will produce a cylindrical workpiece. The tool clamp is a component of lathe that has a function to hold the cutting tool used in the turning process. Where the standard chisel clamp of the lathe generally has transverse, longitudinal or taper movements. While in turning the radius on the lathe there are many obtacles in the process. For this reason, it is necessary to design the radius of the post tool, which is the tool clamp used in turning the radius on the lathe. Where in this research is analyzing the design of the tool post radius on the surface roughness of the S45C steel with variations in the size of the workpiece 20 mm, 50 mm, 80 mm and also the spindle rotation speed of 210 rpm, 380 rpm, and 460 rpm.The results of the study showed that at a diameter of 20 mm the optimal value was obtained at a spindle rotation speed of 460 rpm with an average value of surface roughness wa 0,80 μm. At a diameter of 50 mm the optimal value is obtaindes at a spindle rotation speed of 460 rpm with an average value of surface roughness produced was 1,34 μm. And at a diameter of 80 mm the optimal value is obtained at a spindle rotation speed of 460 rpm with an average value of surface roughness produced is 1,6 μm. It can be see from the results of research that the larger the diameter of worpiece the greater the surface roughness, the greater the spindle rotation speed value of surface roughness decreases. Thus from the research carried out, variations in diameter and spindle rotation at turning radius using the tool post radius affect the value of surface roughness produced. And also the roughness of the object from the radius lathe process using the radius tool post meets the standard permissible roughness value of 0,4 – 5,0 μm. Keywords : Lathe Machine, Radius Tool Post, Surface Roughness

Item Type:	Thesis (Skripsi)
Uncontrolled Keywords:	Keywords : Lathe Machine, Radius Tool Post, Surface Roughness
Subjects:	Engineering > Mechanical Engineering
Divisions:	Fakultas Teknologi Industri > Teknik Mesin S1 > Teknik Mesin S1(Skripsi)