ANALISA PENGARUH CAMPURAN BUAH PINUS DAN TINJA KAMBING DENGAN PEREKAT TETES TEBU TERHADAP KARAKTERISTIK BIO-BRIKET

ADMAJA, FEDLY WIRA (2019) ANALISA PENGARUH CAMPURAN BUAH PINUS DAN TINJA KAMBING DENGAN PEREKAT TETES TEBU TERHADAP KARAKTERISTIK BIO-BRIKET. Skripsi thesis, Institut Teknologi Nasional Malang.

Text SKRIPSI Fedly Wira Admaja (15.11.082).pdf Restricted to Registered users only Available under License Creative Commons Attribution Non-commercial Share Alike. Download (6MB) | Request a copy

Abstract

ANALISA PENGARUH CAMPURAN BUAH PINUS DAN TINJA KAMBING DENGAN PEREKAT TETES TEBU TERHADAP KARAKTERISTIK BIO-BRIKET Fedly Wira Admaja Jurusan Teknik Mesin Fakultas Teknologi Industri Institut Teknologi Nasional, Malang Jl. Raya Karanglo km 2, Malang 65145 Email: wirafedly@gmail.com ABSTRAK Demi mengurangi konsumsi bahan bakar fosil manusia berlomba-lomba membuat bahan bakar alternatif yang dapat ditemukan dengan mudah di alam dan tentunya tidak merusak lingkungan. Biomassa merupakan semua jenis material organik yang dihasilkan dalam proses fotosintesis, kandungan energi yang besar dalam biomassa dapat dimanfaatkan sebagai sumber bahan bakar baru yang dapat diperbaharui. Bahan baku briket yang digunakan adalah buah pinus dan Tinja kambing dengan perekat tetes tebu. Bahan baku digiling menjadi serbuk kemudian dibakar dalam tanur dengan temperatur 2000C dengan lama waktu pengarangan selama 50-100 menit. Pencampuran bahan baku dengan variasi 30gr :100gr : 30gr, 40gr : 100gr : 30gr, 50gr : 100gr : 30gr, 60gr : 100gr: 30gr, 70gr: 100gr: 30gr dan dicetak dengan tekanan pengepresan 25 kg/cm2 setelah itu dioven dengan suhu 700C selama 3 jam 30 menit. Karakteristik biobriket yang dicari yaitu, kerapatan, drop test, nilai kalor, kadar air, dan kadar abu. Dari hasil penelitian ini didapatkan nilai kalor terbaik pada komposisi buah pinus dan Tinja kambing 70gr: 100gr: 30gr yaitu sebesar 6662,36 kal/gr dengan nilai kerapatan 0,90 gr/cm3, nilai drop test briket sebesar 0,09 %, kadar air 3,54%, dan kadar abu 14,30%. Kata Kunci : Bio-biket, buah pinus, Tinja kambing, tetes tebu, nilai kalor. ABSTRACT In order to reduce the consumption of human fossil fuels competing to make alternative fuels that can be found easily in nature and certainly do not damage the environment. Biomass is all types of organic material produced in photosynthesis, a large energy content in biomass can be used as a renewable fuel source. The raw materials of briquettes used are pine cone and goat stool with molasses drops. The raw material is ground into powder and then burned in a furnace at a temperature of 2000C with a length of time of drying for 50-100 minutes. Mixing raw materials with variations 30gr :100gr : 30gr, 40gr : 100gr : 30gr, 50gr : 100gr : 30gr, 60gr : 100gr: 30gr, 70gr: 100gr: 30gr and printed with pressing pressure of 25 kg / cm2 after which it is heated at 700C for 3 hours 30 minutes. Biobriquette characteristics that are sought are, density, drop test, calorific value, water content, and ash content. From the results of this study obtained the best calorific value in the composition of goat and pine fruit 70gr: 100gr: 30gr which is equal to 6662,36 kal / gr with a density value of 0.90 gr / cm3, the drop test value of briquettes is 0.09%, water content 3.54%, and ash content of 14.30%. Keywords : Bio-briquette, pine cone, goat stool, molasses, calorific value.

Item Type:	Thesis (Skripsi)
Uncontrolled Keywords:	Keywords : Bio-briquette, pine cone, goat stool, molasses, calorific value.
Subjects:	Engineering > Mechanical Engineering
Divisions:	Fakultas Teknologi Industri > Teknik Mesin S1 > Teknik Mesin S1(Skripsi)
Depositing User:	Ms Nunuk Yuli
Date Deposited:	04 Dec 2025 04:19
Last Modified:	04 Dec 2025 04:19
URI:	http://eprints.itn.ac.id/id/eprint/15793