ANALISA PATAHAN KOMPOSIT POLYESTER BERPENGUAT SERAT KARBON, AGAVE DAN RAMI DENGAN METODE FTIR DAN MICRO-MACRO

Savio, Benezato Maria (2019) ANALISA PATAHAN KOMPOSIT POLYESTER BERPENGUAT SERAT KARBON, AGAVE DAN RAMI DENGAN METODE FTIR DAN MICRO-MACRO. Skripsi thesis, Institut Teknologi Nasional Malang.

Text SKRIPSI full (5).pdf Restricted to Registered users only Available under License Creative Commons Attribution Non-commercial Share Alike. Download (4MB) | Request a copy

Abstract

ANALISA PATAHAN KOMPOSIT POLYESTER BERPENGUAT SERAT KARBON, AGAVE DAN RAMI DENGAN METODE FTIR DAN MICRO-MACRO Benezato Maria Savio (1511028) Jurusan Teknik Mesin S-1, FTI – Institut Teknologi Nasional Malang Email : benynanarika@gmail.com ABSTRAK komposit merupakan gabungan antar dua bahan yang berlainan untuk memperoleh suatu bahan baru dengan sifat-sifat fisik dan mekanik yang lebih baik dibandingkan sifat komponen pembentuknya. Salah satu jenis komposit yang banyak dihasilkan adalah komposit berpenguat serat alam. Penelitian ini bertujuan untuk menganalisis karakteristik patahan komposit polyester berpenguat serat karbon,agave dan rami,patahan tersebut disebabkan oleh pengujian sifat mekanis uji impak dan tarik. Selanjutnya dilakukan analisis karakteristik patahannya dengan menggunakan metode FTIR dan Micro-Macro. Permasalahan yang dikaji untuk mengetahui pengaruh variasi fraksi berat serat dan susunan serat terhadap FTIR dan Micro-Macro. Dari hasil uji FTIR pada komposit polyester dengan perbandingan tiga variasi fraksi berat serat memiliki gugus fungsi dan daerah serapan yang sama. Hanya menunjukan struktur kristal selulosa di wavenumber 2849 cm-1 dengan nilai transmittance yang meningkat dan menuru yang membedakan terbentuknya struktur kristal selulosa, dan zat pengotor, lignin, hemiselulosa ditunjukan pada bilangan gelombang 1250-1369 cm-1 dengan ikatan C=C Aromatik. Dari variasi berat serat (karbon 30% : 10 agave,rami) merupakan variasi berat serat yang terbaik karena memiliki nilai transmittance yang mencapai 100% dengan menunjukan struktur Kristal selulosa pada wavenumber 2849 cm-1 peak yang muncul lebih runcing dan menyisakan sebagian kadar lignin,hemiselulosa dan zat pengotor lainnya yang ditunjukkan dengan terdapatnya peak pada rentang 1250-1369 cm-1 dengan ikatan C=C Aromatik dan kekuatan sifat mekanis energi impak dan harga impak yang paling tinggi, di bandingkan dengan variasi berat serat (karbon 10%:30% agave,rami), (karbon 20%:20% agave,rami) dengan nilai transmittance yang rendah 99% dan 99,5%. Pengamatan Micro didapatkan bahwa serat agave,rami masih dilapisi oleh kotoran pada struktur kimianya dan serat karbon yang didapat secara tidak sempurna sehingga tiga variasi berat serat dilihat dari orientasi seratnya tidak beraturan dengan berbentuk acak. Pengamatan macro terjadi patahan jenis campuran dari patahan getas dan patahan liat. Kata Kunci : Komposit polyester,serat agave,serat rami,serat karbon,strukrur kimia selulosa,hemiselulosa,lignin,Ftir,Micro-Macro COMPOSITE ANALYSIS OF POLYESTER COMPOSITE WITH CARBON, AGAVE AND HEMP FIBER USING FTIR AND MICRO-MACRO METHODS Benezato Maria Savio (1511028) Bachelor of Mechanical Engineering Department, FTI - National Institute of Technology Malang Email : benynanarika@gmail.com ABSTRACT composite is a combination of two different materials to obtain a new material with physical and mechanical properties that are better than the properties of the forming components. One type of composite that is widely produced is composite reinforced natural fibers. This study aims to analyze the characteristics of carbon fiber, agave and flax reinforced polyester composites, the fracture caused by testing the mechanical properties of impact and tensile tests Then the fault characteristics were analyzed using the FTIR and Micro-Macro methods. The problems studied to determine the effect of variations in fiber weight fraction and fiber arrangement on FTIR and Micro-Macro. The problems studied to determine the effect of variations in fiber weight fraction and fiber arrangement on FTIR and Micro-Macro From the FTIR test results on polyester composites with a comparison of three variations of fiber weight fraction having the same functional group and absorption area. It only shows the cellulose crystal structure at the source 2849 cm-1 with transmittance values increasing and decreasing which distinguishes the formation of cellulose crystal structures, and impurities, lignin, hemicellulose shown at wavenumbers 1250-1369 cm-1 with C=C Aromatic bonds. From variations in fiber weight (carbon 30%:10% agave, hemp) is the best variation in fiber weight because it has a transmittance value that reaches 100% by showing the structure of cellulose crystals on sources 2849 cm-1 peak that appears more pointed and leaves a portion of lignin content, hemicellulose and other impurities indicated by the presence of peaks in the range 1250-1369 cm-1 with C = C Aromatic bonds and the strength of mechanical properties of impact energy and the highest impact price, compared with variations in weight of fiber (carbon 10%:30% agave,hemp),(carbon 20%:20% agave, hemp) with a low transmittance value of 99% and 99,5%. Micro observation found that agave, hemp fibers were still coated with impurities on their chemical structure and carbon fiber was incompletely obtained so that three variations in fiber weight were seen from the orientation of the irregular fibers with random shapes. Macro observations occur with mixed types of brittle faults and clay fractures. Keywords : Polyester composite, agave fiber, hemp fiber, carbon fiber, cellulose chemical structure, hemicellulose, lignin, Ftir, Micro-Macro

Item Type:	Thesis (Skripsi)
Uncontrolled Keywords:	Polyester composite, agave fiber, hemp fiber, carbon fiber, cellulose chemical structure, hemicellulose, lignin, Ftir, Micro-Macro
Subjects:	Engineering > Mechanical Engineering
Divisions:	Fakultas Teknologi Industri > Teknik Mesin S1 > Teknik Mesin S1(Skripsi)
Depositing User:	Ms Nunuk Yuli
Date Deposited:	04 Dec 2025 06:04
Last Modified:	04 Dec 2025 06:04
URI:	http://eprints.itn.ac.id/id/eprint/15810