PENGARUH VARIASI JARAK ANODA DAN KATODA TERHADAP KEKERASAN SERTA KETEBALAN LAPISAN CHROME PADA PLASTIK FIBER GLASS MENGGUNAKAN METODE ELEKTROPLATING

Pribadi, Prayogi Kukuh (2016) PENGARUH VARIASI JARAK ANODA DAN KATODA TERHADAP KEKERASAN SERTA KETEBALAN LAPISAN CHROME PADA PLASTIK FIBER GLASS MENGGUNAKAN METODE ELEKTROPLATING. Skripsi thesis, ITN MALANG.

Text SKRIPSI Dadi campur.docx Restricted to Registered users only Download (3MB)

Abstract

Penggunaan plastik didunia industri berkembang cukup pesat, tetapi material plastik memiliki banyak kelemahan. Untuk mengatasi kelemahan tersebut sekaligus untuk memperoleh sifat mekanik pada plastik seperti sifat konduktor, tahan terhadap abrasi, tahan terhadap cuaca dan memberikan tampilan logam (metallic appearance), maka plastik perlu dilakukan pelapisan. Hard crome merupakan salah satu proses pelapisan (electroplating) dimana benda kerja yang akan dilapisi diposisikan sebagaimana benda kerja (katoda) untuk mendapatkan lapisan yang tebal dan keras pada permukaannya lapisan ini akan meninggalkan permukaan yang keras pada benda kerja tersebut. Tujuan dari penelitian ini adalah untuk mengetahui seberapa besar pengaruh jarak anoda dan katoda terhadap kekrasan dan ketebalan lapisan yang dihasilkan pada permukaan fiber glass. Variabel bebas yang dipakai dalam penelitian ini adalah variabel jarak anoda dengan katoda 5cm, 10cm, dan 15 cm. Serta varibel terikatnya yaitu fiber glass, sedangkan varibel terkontrolnya yaitu temperatur larutan 30° dan waktu 5 menit dan tegangan 5 volt. Hasil penelitian didapatkan bahwa variasi jarak katoda dan anoda berpengaruh terhadap kekerasan hasil pelapisan dan hasil ketebalan yang dihasilkan. Semakin dekat jarak anoda dan katoda pada proses electroplating akan menghasilkan pelapisan yang lebih tebal dan kekerasannya meningkat. Kekerasan dan ketebalan maksimum didapatkan pada jarak 5cm yaitu kekerasan rata-rata 73,2 VHN dan ketebalan rata-rata 71,3 µm Kata kunci : elektroplating fiber glass, hardchrome, jarak anoda – katoda, kekerasan, EFFECT OF VARIATION OF DISTANCE ANODE AND CATHODE OF VIOLENCE AND THICKNESS CHROME COATING ON GLASS FIBER USING PLASTIC ELEKTROPLATING Prayogi Kukuh Pribadi (1), Ir. I Wayan Sujana, MT (2) Student Sechanical Enginering S-1 Institut Teknologi Nasional Malang, e-mail: prayogikp@gmail.com Lecturer Mechanical Enginering S-1 Institut Teknologi Nasional Malang ABSTRACT The use of plastics in the industry developed rapidly, but the plastic material has many disadvantages. To overcome these weaknesses as well as to obtain mechanical properties in plastics such as the nature of the conductor, resistant to abrasion, resistant to weather and give the appearance of metal (metallic appearance), the plastic coating needs to be done. Is one of the hard chrome plating process (electroplating) in which the workpiece to be coated is positioned as the workpiece (cathode) to obtain a thick and hard layer on the surface of this layer will leave a hard surface on the work piece. The aim of this study was to determine how much influence within the anode and cathode of the hardness and thickness of the resulting layer on the surface of the glass fiber. The independent variable used in this study is variable anode to cathode distance of 5cm, 10cm and 15 cm. As well as the dependent variable, namely fiber glass, while the uncontrolled variables that solution temperature of 30 ° and 5 minutes and 5 volts. The result showed that the variation within the cathode and anode effect on the result of coating hardness and thickness of the resulting proceeds. The closer the anode and cathode in the electroplating process will produce a thicker coating and hardness increase. Violence and the maximum thickness is obtained at a distance of 5cm that violence VHN average of 73.2 and an average thickness of 71.3 μm.

Item Type:	Thesis (Skripsi)
Uncontrolled Keywords:	elektroplating, distance anode - cathode, fiber glass hardchrome, violence
Subjects:	Engineering > Mechanical Engineering
Divisions:	Fakultas Teknologi Industri > Teknik Mesin S1 > Teknik Mesin S1(Skripsi)
Depositing User:	Dewi Saraswati
Date Deposited:	10 Dec 2025 06:55
Last Modified:	10 Dec 2025 06:55
URI:	http://eprints.itn.ac.id/id/eprint/15954

Actions (login required)

View Item